Electronic Materials Letters , vol. 4, no. 3, pp.135-139, September, 2008
DOI :
Magnetic Properties of Fe-Pt Films Electrodeposited by Diffusion Control
Fei Li1, Tae Hoon Kim1, Bon Heun Koo1, Chan Gyu Lee1,*, and Toshitada Shimozaki2 1Changwon National University, 2Kyushu Institute of Technology
Abstract : Fe-Pt films were produced by a simple method of electrodeposition under diffusion control, using a novel bath system containing small amounts of Fe2+ and PtCl62-. The films were annealed and, their structure and magnetic properties were studied. The sample started to show some ordering at a temperature less than 550กษ, which is lower than the previously reported ordering temperature. A coercivity of 3.2 kOe, comparable to previous data, and a squareness of 0.7 were obtained after the film was vacuum-annealed at 550กษ for 15 min. The films displayed a longitudinal magnetic anisotropy. The obtained results promise this method to be a new choice for electrodeposition of Fe-Pt films.
Keyword :
Fe-Pt, electrodeposition, diffusion control, L10 structure, magnetic properties
|